Titanium dioxide as used in sunscreens is commonly modified with other ingredients to ensure efficacy and stability. Examples of what are known as surface modifier ingredients used for titanium dioxide include stearic acid, isostearic acid, polyhydroxystearic acid, and dimethicone/methicone copolymer.
Lithopone is produced by coprecipitation of barium sulfate and zinc sulfide. Most commonly coprecipitation is effected by combining equimolar amounts of zinc sulfate and barium sulfide:
There seems to be a lot of misunderstanding about titanium dioxide, which can be used as a colorant in foods. While headlines may suggest titanium dioxide is a health concern, scientific research has actually shown titanium dioxide to be safe. So what is it used for and why is it used? Read on to learn more!
A great number of other brands with fancy names have gone out of the German market, because of some defects in the processes of manufacture. The English exporters, as a rule, offer three or four grades of lithopone, the lowest priced consisting of about 12 per cent zinc sulphide, the best varying between 30 and 32 per cent zinc sulphide. A white pigment of this composition containing more than 32 per cent zinc sulphide does not work well in oil as a paint, although in the oilcloth and shade cloth industries an article containing as high as 45 per cent zinc sulphide has been used apparently with success. Carefully prepared lithopone, containing 30 to 32 per cent sulphide of zinc with not over 1.5 per cent zinc oxide, the balance being barium sulphate, is a white powder almost equal to the best grades of French process zinc oxide in whiteness and holds a medium position in specific gravity between white lead and zinc oxide. Its oil absorption is also fairly well in the middle between the two white pigments mentioned, lead carbonate requiring 9 per cent of oil, zinc oxide on an average 17 per cent and lithopone 13 per cent to form a stiff paste. There is one advantage in the manipulation of lithopone in oil over both white lead and zinc oxide, it is more readily mis-cible than either of these, for some purposes requiring no mill grinding at all, simply thorough mixing with the oil. However, when lithopone has not been furnaced up to the required time, it will require a much greater percentage of oil for grinding and more thinners for spreading than the normal pigment. Pigment of that character is not well adapted for use in the manufacture of paints, as it lacks in body and color resisting properties and does not work well under the brush. In those industries, where the paint can be applied with machinery, as in shade cloth making, etc., it appears to be preferred, because of these very defects. As this sort of lithopone, ground in linseed oil in paste form, is thinned for application to the cloth with benzine only, and on account of its greater tendency to thicken, requires more of this comparatively cheap thinning medium, it is preferred by most of the manufacturers of machine painted shade cloth. Another point considered by them is that it does not require as much coloring matter to tint the white paste to the required standard depth as would be the case if the lithopone were of the standard required for the making of paint or enamels. On the other hand, the lithopone preferred by the shade cloth trade would prove a failure in the manufacture of oil paints and much more so, when used as a pigment in the so-called enamel or varnish paints. Every paint manufacturer knows, or should know, that a pigment containing hygroscopic moisture does not work well with oil and driers in a paint and that with varnish especially it is very susceptible to livering on standing and to becoming puffed to such an extent as to make it unworkable under the brush. While the process of making lithopone is not very difficult or complicated, the success of obtaining a first class product depends to a great extent on the purity of the material used. Foreign substances in these are readily eliminated by careful manipulation, which, however, requires thorough knowledge and great care, as otherwise the result will be a failure, rendering a product of bad color and lack of covering power.
Overnight news titanium dioxide industry
sachtleben tio2 manufacturer. By collaborating with industry experts and investing in scientific research, they have developed specialized TiO2 grades tailored for specific customer needs. These include high-gloss TiO2 for automotive paints, ultra-fine grades for printing inks, and even TiO2 variants designed for use in food and pharmaceuticals, adhering to stringent safety regulations.In addition to hiding power, titanium dioxide also plays a vital role in enhancing the durability of paints. It acts as a barrier, protecting the walls from external elements such as UV radiation, moisture and pollutants. Titanium dioxide's high refractive index allows it to reflect harmful UV rays, preventing them from fading paint and retaining its vibrant colors for a long time. This UV resistance is especially important for facades that are exposed to sunlight throughout the day.
As early as sixty years ago, zinc sulphide was first thought of as a pigment for coloring India rubber and a patent for the process of its manufacture was issued in England. But it was not until twenty years later that zinc sulphide and its manufacture was seriously considered as a pigment for paint, and in 1874 a patent was issued for a process of manufacturing a white pigment, composed of zinc sulphide and barium sulphate, known as Charlton white, also as Orr's white enamel. This was followed in 1876 by a patent issued to a manufacturer named Griffith and the product, which was similar in character to Charlton white, was known as Griffith's patent zinc white. In 1879 another patent for a more novel process was obtained by Griffith & Cawley, the product made under this process proving the best of the series placed upon the market up to that date. After that time many new processes were patented, all, however, tending to the same object, that of producing a white pigment, composed of zinc sulphide and barium carbonate, the results, however, in many cases ending with failure.